Technical Data

 

产品说明

Versaflex™ HC 1110-60 Clear EU is a clear, medical compliant overmold designed to adhere to multiple substrates.

 

• Excellent bond to PC, ABS, PC/ABS, PC/PETG, and PC/PBT 

• Rubber Feel 

• Soft Touch 

 

总览

材料状态 • 已商用：当前有效

资料 1 • Technical Datasheet

搜索 UL 黄卡 •  普立万公司

• Versaflex™

供货地区 • 欧洲

特性 • 良好的成型性能 • 良好的加工性能 • 清晰度，高

• 良好的加工稳定性 • 良好的着色性

• Transparent Parts • 个人护理 •

用途 • 包覆成型 • 透明或半透明配件 医疗/护理用品

• 电气/电子应用领域 • 消费品应用领域

机构评级 • FDA 未评级 2

RoHS 合规性 • RoHS 合规

外观 • 清晰/透明

形式 • 粒子

加工方法 • 注射成型

物理性能 额定值(英制) 额定值(公制) 测试方法

密度 / 比重 0.900 0.898g/cm³ ISO 1183

弹性体 额定值(英制) 额定值(公制) 测试方法

拉伸应力 4 DIN 53504

300%应变, 73°F (23°C), 0.0787 in (2.00 mm) 580psi 4.00MPa

抗张强度 4 (断裂, 73°F (23°C)) 1350psi 9.30MPa DIN 53504-S2

伸长率 4 900% 900% DIN 53504

(断裂, 73°F (23°C), 0.0787 in (2.00 mm))

压缩永久变形 (73°F (23°C), 72 hr) 30% 30% ISO 815

硬度 额定值(英制) 额定值(公制) 测试方法

肖氏硬度 (邵氏 A, 10 秒, 73°F (23°C)) 60 60 ISO 7619

充模分析 额定值(英制) 额定值(公制) 测试方法

表观粘度 (392°F (200°C), 11200 sec^-1) 22.0Pa·s 22.0Pa·s ASTM D3835

注射 额定值(英制) 额定值(公制)

建议的最大回制料比例 20% 20%

料筒后部温度 350 到 420°F 177 到 216°C

料筒中部温度 360 到 430°F 182 到 221°C

料筒前部温度 380 到 450°F 193 到 232°C

射嘴温度 400 到 470°F 204 到 243°C

模具温度 70 到 90°F 21 到 32°C

背压 75.0 到 175psi 0.517 到 1.21MPa

螺杆转速 75 到 125rpm 75 到 125rpm

 

Versaflex™ HC 1110-60 Clear EU

热塑性弹性体

普立万公司

 

注射说明

Versaflex™ HC 1110-60 Clear EU can use a variety of color concentrates. The type of color concentrates most suitable for the application are dependent upon the grade and the specific substrate materials, including color concentrate and filler levels. It is therefore advisable to contact your GLS Technical Representative to discuss your particular application. It should be noted that some color concentrates may affect adhesion to the substrate, resulting in decreased peel strength. Concentrates based on PVC should not be used. The final determination of color concentrate suitable should be determined by customer trials.

 

Purge thoroughly before and after use of this product with a low flow (0.5-2.5 MFR) polyethylene (PE) or polypropolene (PP).

 

Versaflex™ HC 1110-60 Clear EU can use regrind up to 20% with minimal property losses, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer.

 

Versaflex™ HC 1110-60 Clear EU has good melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer.

 

Drying is not Required

 

Injection Speed: 1 to 5 in/sec

1st Stage - Boost Pressure: 180 to 580 psi 2nd Stage - Hold Pressure: 50% of Boost Hold Time (Thick Part): 4 to 10 sec

Hold Time (Thin Part): 1 to 3 sec

 

 

 

 

 

 

TPE Versaflex™ HC 1110-60 Clear EU ,热塑性弹性体TPE,包胶热塑性弹性体TPE,包胶PP热塑性弹性体TPE,包胶PA尼龙热塑性弹性体TPE,包胶PA6热塑性弹性体TPE,包胶PA66热塑性弹性体TPE,包胶POM热塑性弹性体TPE,包胶PE热塑性弹性体TPE,包胶ABS热塑性弹性体TPE,包胶PC+ABS热塑性弹性体TPE,包胶PC热塑性弹性体TPE,包胶PS热塑性弹性体TPE,包胶ASA热塑性弹性体TPE,包胶PMMA热塑性弹性体TPE,包胶SAN热塑性弹性体TPE,包胶PBT热塑性弹性体TPE,包胶PPO热塑性弹性体TPE,包胶热塑性弹性体TPE是东莞市双帮塑胶原料有限公司常年销售的塑料,因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表,SGS报告,COA原料出厂报告,REACH报告,SVHC报告,生物兼容报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123，微信：13549213581  QQ：15397858    13549213581 肖生