Amodel® AT-1001L    
    
聚二甲苯酰胺    
    
Solvay Specialty Polymers   
     
 Technical Data    
     

产品说明

Amodel® AT-1001L is an unreinforced, impact modified polyphthalamide (PPA) resin that exhibits exceptional impact strength at temperatures ranging from room temperature to as low as -40°F (-40°C), which suggests possible applications in ski boots and hockey skates.

In addition, its chemical and wear resistance, combined with good mechanical properties, make Amodel® AT-1001L resin a prime candidate for applications such as anti-friction and wear resistant components, chemical, oil field, automotive and safety equipment.

• Natural: AT-1001 L NT

总体

材料状态 • 已商用:当前有效   
资料 1 •  Technical Datasheet
  
搜索 UL 黄卡 •  Solvay Specialty Polymers
  
 •  Amodel®
  
    
供货地区 • 北美洲 • 南美洲 • 亚太地区 
 • 非洲和中东 • 欧洲  
    
添加剂 • 冲击调节器 • 润滑剂 • 脱模 
 • 低翘曲性 • 耐低温撞击 • 透湿性强 
性能特点 • 改良抗撞击性 • 耐化学性良好  
   • 延展性 
 • 经润滑 • 耐磨损性良好  
    
 • Oil/Gas Applications • 金属置换 • 设备/机械部件 
用途 • 工业领域: • 汽车电子 • 型号 
 • 工业配件 • 汽车领域的应用: • 一般目的 
RoHS 合规性 • 联系制造商   
外观 • 自然色   
形式 • 颗粒料   
加工方法 • Water-Heated Mold Injection • 注射成型  
 Molding   
    
 
多点数据 • Isothermal Stress vs. Strain 
 (ISO 11403-1) 
  
 

• Secant Modulus vs. Strain (ISO 11403-1)
 

物理性能 额定值单位制 测试方法
密度 1.11g/cm³ ISO 1183/A
收缩率  ASTM D955
流动 1.7 到 2.2% 
横向流动 1.9 到 2.1% 
吸水率 (24 hr) 0.75% ASTM D570
机械性能 额定值单位制 测试方法
拉伸模量 1900MPa ASTM D638
抗张强度 (断裂) 62.1MPa ASTM D638
伸长率  ASTM D638
屈服 6.0% 
断裂 30% 
弯曲模量 2210MPa ASTM D790
弯曲强度 96.5MPa ASTM D790
泊松比 0.35 ASTM E132
冲击性能 额定值单位制 测试方法
悬壁梁缺口冲击强度  ASTM D256
-40°C 750J/m 
23°C 1100J/m 
热性能 额定值单位制 测试方法
热变形温度 (1.8 MPa, 退火, 3.18 mm) 120°C ASTM D648
熔融温度 310°C 

 
 
 
 
 
 
 
Amodel® AT-1001L      
聚二甲苯酰胺      
      
Solvay Specialty Polymers   
        
  补充信息      
        
  Penetration Impact, ASTM D3763, 73°F, Maximum Load: 1100 lbs      
  Penetration Impact, ASTM D3763, 73°F, Total Energy Absorbed: 40 ft-lbs      
  Penetration Impact, ASTM D3763, 73°F, Energy to Maximum Load: 30 ft-lbs      
  Penetration Impact, ASTM D3763, -10°F, Total Energy Absorbed: 40 ft-lbs      
  Penetration Impact, ASTM D3763, -10°F, Maximum Load: 1260 lbs      
  Penetration Impact, ASTM D3763, -10°F, Energy to Maximum Load: 30 ft-lbs      
     
  注射  额定值单位制 
  干燥温度  110°C 
  干燥时间  4.0hr 
  建议的最大水分含量  0.045%    
  料筒温度  79.4°C 
  螺筒后部温度 304 到 318°C 
  螺筒前部温度 316 到 329°C 
  加工(熔体)温度 321 到 343°C 
  模具温度 65.6 到 110°C